Biological Effect of Some Metal Oxides Nanocomposites on Saccharomyces Cerevisiae

Анотація

The effect of three types of nanostructured metal-containing saponite clays on brewer’s yeast, Saccharomyces cerevisiae, was investigated. The experimental data show that the studied materials, even though they possess nanometre-sized particles, do not have any inhibitory effect on organisms. In these study a significant increase in the number of cells for S. cerevisiae was demostrated. The largest concentration of cells has been recorded under the influence of a niobium-containing clay, prepared from niobium pentaethoxide at a concentration of 2 mg ml^-1. Under these conditions the number of cells was increased up to 5 times in comparison to the control. According to the MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) test, the best results were obtained for both the proton-exchanged and niobium-containing saponite solids at a concentration of 0,5 mg ml^-1. They are relatively controlled stimulate mitochondrial reductase activity of yeast cells.

Исследовано влияние трех типов наноструктурированных металлосодержащих сапонитовых глин на жизнеспособность пивных дрожжей Saccharomyces cerevisiae. Экспериментальные данные показывают, что исследуемые материалы, несмотря на то, что они нанометрового размера, не проявляют ингибирующее действие на организмы. В исследовании продемонстрировано значительное увеличение количества клеток для S. cerevisiae за действия наноматериалов. Наибольшая концентрация клеток была зарегистрирована при действии нанокомпозита Nb-Sap-EtO в концентрации 2 мг/мл, в этих условиях, количество клеток было увеличено до 5 раз по сравнению с контролем. По данным МТТ теста наблюдается стимулирование активности митохондриальных редуктаз в пивных дрожжах при влиянии наноматериалов, которые содержат в своем составе ниобий в концентрациях от 0,5 мг/мл.